Duplex 2507 Forgings are dual phase austenitic-ferritic duplex components manufactured from alloy containing chromium, nickel and molybdenum with restricted carbon content and minimum PREN 42. SAF 2507 Forgings have high strength, resistance to pitting, stress corrosion cracking, erosion and corrosion fatigue, crevice corrosion resistant.
| Grades | UNS DesignationB | TypeB | C | Mn | P | S | Si | Cr | Ni | Mo | N | Other Elements |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Duplex 2507 Grade S32760 | S32760 | . . . | 0.030 | 1.00 | 0.030 | 0.010 | 1.00 | 24.0-26.0 | 6.0-8.0 | 3.0-4.0 | 0.20-0.30 | Cu 0.50-1.00, W 0.50-1.00, %Cr+3.3x%Mo +16x%N≥40 |
| UNS Designation | Solution Temperature, °F [°C]B,C | Size Range | Mechanical Properties | ||||
|---|---|---|---|---|---|---|---|
| Tensile Strength,ksi [MPA] | Yield Strength,ksi [MPA] | Elongation in 2″[50 mm] or 4D % | HardnessD | ||||
| Rockwell, HRC maximum | Brinell, maximum | ||||||
| S32760 | 2010 [1100] | . . . | 109 [750] | 80 [550] | 25 | 30 | 290 |